Distinctive points:

A water-based rust preventive coating that is formulated using plant-based polymer technology to provide outstanding protection against corrosion on both ferrous and nonferrous metals.
The product leaves an attractive black satin finish.
The normal duration of protection is up to 3 years.
The surface on which the protective coating will be applied should be prepared clean and dry.
It should be used in a well-ventilated area. There must not be too much air passing through.

6228 KATS Rust Protective Coating (Satin Black)

- Prevent rust and corrosion on metal surfaces.
- Vehicle underbody coating.
- Protection of machine components during storage.
- Protection of metal stock.
- Protection of outdoor stored gear.
1. Passed the ASTM D-2247 test (Humidity Exposure) with results is a chance of rust occurring on the coated surface at less than 0.01% even after exposure to moisture for over 500 hours.

2. Passed the ASTM B-117 test (Corrosion test with chamber) has found that there is a chance of rust occurring on the coated surface is less than 0.01% even after spraying salt vapor for over 50 hours.

3. From the ASTM D-1475 test (determining viscosity or density), it was found that the viscosity value at 8.7 pounds/gallon (1.044 grams/cubic cm).
1. Can be used in ambient temperature or surface temperature of 7° - 38°C. The ideal surface temperature is between 16° - 27°C.

2. Make sure before coating the workpiece that it is completely dry. To reduce temperature and humidity.

3. The film thickness while still wet is 127 - 254 microns and has the thickness of the film when dry is 25.4 - 50.8 microns.

4. Can be used to coat over 3.9 - 7.9 square meters of surface per gallon (1 liter).

Applications